Alloy 230 is a nickel alloy, made up of mostly nickel and chromium, with smaller amounts of tungsten and molybdenum. This combination of metals results in a number of desirable properties including excellent strength, oxidation resistance at temperatures of up to 2,100 °F (1,150 °C) and nitriding-resistance. Alloy 230 is one of the most nitriding-resistant alloys available.[1]
Composition
edit| % | Nickel (Ni) | Chromium (Cr) | Tungsten (W) | Molybdenum (Mo) | Cobalt (Co) | Aluminium (Al) | Lanthanum (La) | Manganese (Mn) | Carbon (C) | Silicon (Si) |
|---|---|---|---|---|---|---|---|---|---|---|
| Min | 47 | 20 | 13 | 1 | - | 0.2 | 0.005 | 0.3 | 0.05 | 0.25 |
| Max | 65 | 24 | 15 | 3 | 5 | 0.5 | 0.005 | 1 | 0.15 | 0.75 |
Properties
editAlloy 230 is also identified by the UNS number UNSN06230. It displays excellent strength at high temperatures, which is why it is often used in high temperature applications such as combustion linings on turbine engines, burner flame shrouds and furnace retorts. It also displays oxidation resistance at temperatures of up to 2,100 °F (1,150 °C), which again makes it ideal for high temperature applications. Its exceptional nitriding-resistance also makes it the preferred choice for nitriding furnace internal parts, as it remains unaffected by the treatment. It is also easily weldable and can be formed by hot or cold-working.
References
edit- ^ Mathias, Paul M. (15 March 1996). "Molecular modeling in engineering design and materials development". Fluid Phase Equilibria. 116 (1–2): 225–236. doi:10.1016/0378-3812(95)02891-9. Retrieved 11 July 2022.